ASTM G103-97(2023)e1

Standard Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution

ASTM International , 01/15/2023

Publisher: ASTM

File Format: PDF

$25.00$50.00

Description

Standard By:ASTM International , 01/15/2023

Published:01/15/2023

Pages:4

File Size:1 file , 220 KB

Language:English

Note:This product is unavailable in Russia, Ukraine, Belarus

1.1This practice primarily covers the test medium which may be used with a variety of test specimens and methods of applying stress. Exposure times, criteria of failure, and so on, are variable and not specified.

1.2This stress-corrosion testing practice is intended for statically loaded smooth non-welded or welded specimens of 7XXX series Al-Zn-Mg-Cu alloys containing less than 0.26 % copper.

1.3The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. See Section 8 for additional precautions.

1.5This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM G103-97(2023)e1

Standard Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution

ASTM G103-97(2023)e1 History

ASTM G103-97(2023)e1

ASTM G103-97(2016)

ASTM G103-97(2011)

More ASTM Standards PDF

DIN 43531 - DRAFT

DIN 18309

DIN 14662

DIN 14800-18 Supplement 7 - DRAFT